Selective growth of single-walled carbon nanotubes and fabrication of devices on their base

O. Kononenko¹, V. Matveev¹, V. Volkov¹, An. Firsov¹, A. Il'in¹, D. Matveev², Y. Kasumov¹, I. Khodos¹
IMT RAS¹ and ISSP RAS², Chernogolovka, Russia
Equipment: SEM Zeiss EVO 50

The samples were fabricated as follows. At first, a Pt film with Cr underlayer was deposited by e-beam evaporation on oxidized silicon wafer using photolithography mask to form contact pads and lanes. Then the wafer was cut up to obtain chips. 10 nm Al/1 nm Fe bilayer catalyst was selectively deposited by e-beam gun onto the chips using electron beam lithography and a lift-off technique. After that the chips with deposited bilayer catalyst were heated in a furnace in air atmosphere for 2 min in order to form Fe nanoparticles. Then the nanotubes were synthesized by single injection of acetylene CVD technique. E-beam lithography with NanoMaker system and a lift-off process were used to pattern e-beam evaporation deposited Pd-Al electrodes contacting nanotubes.

General view of a sample. 6 nanotube SQUID prototypes.

More images from other authors

A. Firsov; Helmholtz-Zentrum Berlin für Materialien und Energie GmbH, BESSY II A part of Bragg-Fresnel zone plate designed for X-ray optics and spectroscopy...

G.Goltsman, K. Smirnov, N.Kaurova et al.; MSPU, Moscow Superconducting Hot-Electron Bolometer Mixer for Terahertz Heterodyne Receivers...

J. Kouba; Helmholtz-Zentrum Berlin für Materialien und Energie GmbH, BESSY II Hexagonal lattice type photonic crystal in Si3N4...

V. Gurtovoi, A. Firsov; IMT RAS, Chernogolovka Quantum state detector...

A. Nashchekin, E. Arakcheeva, E. Tanklevskaya; Ioffe Physico-Technical Institute RAS, St. Petersburg Two-dimensional semiconductor photonic crystal with a hexagonal lattice of submicrometer holes ...